PRODUCTS > Products > Vapor Barrier (Laminated Insulation Facing) > Alum.-Glass Cloth Facing
AGE-1812
Product & Application
A premium grade Heat-Sealing Alum.-Glass Cloth Facing, tough and durable. It consists of 18u aluminum foil, 8x8 mesh/cm glass cloth as well as heat-activated polyethylene on its back. Suitable for in-line heating lamination with insulation materials. No need applying extra adhesive. Good abrasion and corrosion resistance.
Facing Composition
|
Facing Composition |
Description |
Value (English) |
Value (Metric) |
|
Foil |
Aluminum |
0.72 mil |
18 micron |
|
Adhesive |
F/R Glue |
0.4 mil |
10 micron |
|
Glass Cloth |
8x8 mesh/cm |
558 lbs / 3000 ft2 |
90 gsm |
|
Heat-Activated Coating |
Polyethylene |
1.5 mil |
37.5 micron |
Typical Physical Properties
|
Physical Properties |
Test Method |
Value (English) |
Value (Metric) |
|
Basis Weight |
Scale |
37 lbs / 1000 ft2 |
180 gsm |
|
Permeance (WVTR) |
ASTM E96, Procedure A |
0.02 perm |
1.15 ng/N.s |
|
Tensile Strength - MD |
ASTM D828 |
60 lbs/In |
265 N/25mm |
|
Tensile Strength - XD |
ASTM D828 |
41 lbs/In |
180 N/25mm |
|
Burst Strength |
ASTM D774 |
181 psi |
125 N/cm2 |
|
Low Temperature Resistance |
ASTM D1790 4 hrs @-40 °F (- 40 °C) |
Remains Flexible No Delamination |
Remains Flexible No Delamination |
|
High Temperature Resistance |
ASTM D1790 4 hrs @ +240 °F (+116 °C) |
Remains Flexible No Delamination |
Remains Flexible No Delamination |
|
Dimensional Stability |
ASTM D1204 @ 150F (65C) |
Less than 0.5% |
Less than 0.5% |
|
Emissivity |
ASTM E408 |
0.03 |
0.03 |
Available Roll Width: 1.2m
Remarks
1. The data above are typical values only, and should not be used for specifications purpose.
2. Tolerance: Weight and Thickness: ±10%; Width: ±3mm; Length: Log Roll: ±0.3m, Jumbo Roll ±0.5%.
3. The products should be stored at room temperature, kept away from wet and heat source.
4. The users should take test and do trial-application on the above products before coming into application so as to witness and ensure suitability for their special purpose and technique.